Home > Application & Technology > Heavy Machinery> NDT of heavy plate Mechanical Properties and Cold Ends detection
Leave a Message

NDT of heavy plate Mechanical Properties and Cold Ends detection

Background and requirements

Heavy plate with a slab thickness of up to 400 mm or more is produced in nearly all unalloyed and alloyed steel grades today. The diverse range of properties, e.g., yield strengths from 200 to more than 1100 N/mm2 ensures the precise suitability for use in bridges, high rise buildings, offshore platforms, ship building, line pipes, pressure vessels, heavy-duty machines, and much more. In order to reduce the constructive thicknesses and, with it, the self-weight of a construction, higher-strength steel grades are increasingly requested, while the weldability and the cold toughness must still be acceptable.

For the production of such steel grades, modern manufacturing processes, such as water/air quenching and tempering, accelerated cooling, normalizing, and thermo-mechanical rolling are applied. The customer asks for geometrical and mechanical properties, which are uniform across product length and width, especially for these high-value grades. Consequently, high demands are made on the determination and documentation of product quality.

Site Photo of heavy Thick Plate Production in Steel Plant

Comprehensive dimensional, shape, and surface inspections already take place within the production flow directly on the plate. On the other hand, it is still necessary to extract tests coupons from the edges of the un-trimmed plate in order to determine the mechanical properties. Tensile and toughness tests are performed according to the codes and delivery from highly qualified and certified personnel and they cannot be integrated into online closed loop control with direct feedback. Costs in the range of several thousands of Euros per year arise in a mid-sized heavy plate plant from coupon scrap alone. For these reasons, heavy plate producers are eager to replace the mechanical testing of coupons by nondestructive technology, allowing for these tests to be transferred from the laboratories of quality assurance to the shop floor.

Application Technology

In first projects, a 3MA system was integrated into a trolley, allowing for 3MA tests to be performed on plates moving on the roller conveyor line in the steel plant. Figure below shows this device. A brushing device was integrated into the trolley in order to the remove scale that otherwise represents a strong disturbing influence.

3MA Nondestructive scanning truck for mechanical properties of heavy plates 3MA remote console of heavy plate scanning vehicle

Remote application of the 3MA system in the roller conveyor line of a steel plant: (a) 3MA inspection trolley and (b) remote control desk

Calibration was done on coupons that were taken from the running production. It was apparent that the best results could be achieved if individual calibration functions were used for each steel grade and each plate thickness. In this case, the RMSE was in the range of 4 HB (Brinell hardness) for hardness determination, 10 MPa for Rm, and 20 MPa for Rp0.2.

The main objective of a second project was to avoid pseudo-scrap in heavy plate by the precise detection of the so-called cold ends in the mother plate after rolling. This is shown in Figure below. Cold ends are developing due to altered cooling conditions and at the plate ends. The cold ends are characterized by impaired mechanical properties (Rm and Rp0.2). Therefore, they have to be removed in order to assure a plate that fulfills the quality requirements over the entire length. For this purpose, large sections—usually much larger than the cold ends—are cut off. Due to these safety margins, pseudo-scrap is produced, i.e., material, which still fulfills the requirements on material conformity, is unnecessarily removed and scrapped. In order to avoid this pseudo-scrap, the extension of the cold ends has to be precisely detected. This can be accomplished by 3MA.

Scanning heavy steel plates with 3MA to reduce steel scrap costs

Avoiding pseudo-scrap by precise detection of the extension of cold ends.

The plates that were investigated in this project were steel grades showing a pronounced anisotropy of material properties due to a rolling texture. Therefore, it turned out to be useful to combine the measuring information from 3MA with measuring parameters that are derived from the time‐of‐flight (TOF) measurements of ultrasound (US) waves. It could be shown that, in highly texturized steel grades, adding relative differences of the US TOFs to the calibration functions could reduce the measuring error. This is shown in the following Table.

Parameters in Calibration Functions RMSE of Rm
[MPa]
RMSE of Rp0.2
[MPa]
RMSE of Hardness
[HB]
Only 3MA parameters
12
23
5
3MA and US parameters
10
11
4

Results of different types of calibration—without and with ultrasound (US) parameters.

The calibrated 3MA + US combination system makes it possible to determine the cold ends before cutting by precisely detecting the positions of the acceptance lines, which are separating OK and NOK quality material at the head and the root of the plate. Figure below shows the corresponding measuring procedure. In a first step, the value of the assessing measuring quantity (here: tensile strength, Rm) is measured in the reference point in the middle of the plate. Subsequently, the 3MA + US system is moved stepwise from the edge to the middle until the value of the measuring quantity falls below a preset threshold level, which is the value at the reference point plus a specified margin (here: ?Rm = 15 MPa). Afterwards, the acceptance line has been reached and it can be drawn on the plate.

3MA NDT detection procedure for the cold end at the head and root

Measuring procedure for determining the cold ends at the plate head and at the plate root.

For more information, please contact LAB GAGES, or go on to visit our 3MA series NDT Systems Center.

Recommended products

3MA-X8 System for Fast Materials Characterization

Steel manufacturing and steel processing industries require NDT methods for quality control. Hardness, case depth, strength, and residual stresses are major quality features in demand. The 3MA-X8 inspection system is especially zeroing in on high measurement velocity and variable sensor shaping, allowing to deal with multiple measuring positions or to accelerate area scans.

more
Contact Us
Address:311, Building 5, No.81, Meiyue Road, Waigaoqiao, Free Trade Zone, Pudong, Shanghai, China
E-mail:Amy@labgages.com
Telephone:021-50473900
Phone:18621180929

311,Building 5,No.81,Meiyue Road,Waigaoqiao Free Trade Zone,Pudong,Shanghai,China

amy@labgages.com

021-50473900